Unidirectional
Areal weight (dry): 130 g/m²
Width: 50 cm
Resin content: 35 %
Carbon fiber/ Epoxy-Prepreg 130/500
HT Carbon Areal Weight: 130 g/m²
Tensile strength carbon fiber: 4100 MPa
Tensile modulus carbon fiber: 240 GPa
Fiber orientation unidirectional
Epoxy Resin Content: 35 % w/w, 120°-system
Width: 500 mm
Curing temperature: 80-150°C
Typical properties of a composite laminate:
Tensile Strength : 1800 MPa
Tensile Modulus: 139 GPa
ILS Strength: 73 MPa
Density: 1.57 g/cm3
Single layer thickness: Around 0,12mm
All values given are to be viewed as guidelines and we assume no obligation or liability in connection with this information. The results also depend on the production conditions; we always recommend carrying out your own tests.